Overcoming the thermal conductivity versus oxidation resistance barrier in high-temperature steels

Heat-resistant steels with high chromium additions (≥5 weight percent) are critical for many high temperature energy and manufacturing applications, including heat exchangers, pistons for engines, and dies for metal working and casting. However, while high chromium additions increase oxidation resistance at elevated temperatures, they also compromise thermal conductivity, resulting in a metallurgical trade-off between these two important properties. Here we show that a microstructure with both higher thermal conductivity and improved oxidation resistance at elevated temperatures is achieved in a unique steel with only 1 weight percent chromium, thereby overcoming the long-standing metallurgical trade-off. This is accomplished through a tailored thermal treatment that produces a tempered martensitic matrix with low solute content and a fine dispersion of copper precipitates and molybdenum enriched carbides. A further discovery is that the resultant thermally grown oxide includes an iron-copper-manganese-enriched outer layer that provides high-temperature oxidation protection equivalent to heat-resistant steels with five times the chromium content and 25% lower thermal conductivity.