Magnetic-assisted welding enhances joint strength by 14% and energy absorption by 30% in high-strength steel joints, suggesting improved structural performance.
H1000 stainless steel is defined as a nickel-saving austenitic stainless steel, characterized by high strength and high elongation. DP590 steel is widely used in the manufacturing of vehicle bodies. DP590 dual-phase steel is classified as a high-strength low-alloy steel, known for its high strength and good formability. To address issues such as nugget deviation, inhomogeneous mixing of the internal nugget microstructure, and interfacial fracture during tensile-shear testing in resistance spot-welded joints of these dissimilar materials, a unilateral magnetic-assisted resistance spot-welding process was proposed. The influence of the external magnetic field on various properties of the joint was systematically investigated. The results indicate that the application of an external magnetic field significantly enhances the strength of H1000/DP590 dissimilar spot-welded joints, with joint strength increasing by approximately 14% and energy absorption capacity improving by about 30%. These improvements are attributed to the electromagnetic stirring effect induced by the magnetic field, through which the effective nugget diameter was enlarged, the microstructure was homogenized, and the macroscopic morphology of the nugget was modified. As a result, the bonding area between the nugget and the base metal is expanded, and the fracture mode of the joint is shifted from interfacial failure to partial button failure, thereby enhancing the mechanical properties of the joint.
No takes yet. Share an insight, caveat, or question.
Feng et al. (2025) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: