Study on the Effect of Laser Shock Angle on Surface Integrity and Wear Performance of H13 Steel

The internal surfaces of hot-working dies are prone to wear and fatigue fracture during service, often necessitating surface modification and strengthening. Among available techniques, laser shock peening (LSP) is an effective surface strengthening method. However, when treating internal surfaces, achieving perpendicular laser incidence is difficult, and irradiation must often be applied at an angle. To clarify the relationship between the laser incidence angle and the strengthening effect, this study applied laser shock peening to H13 steel at various incidence angles(0°, 15°, 30°, 45°) with a spot diameter of 3 mm, using laser energies of 8 J, 8.2 J, 9.2 J, and 11.3 J, respectively, and maintaining a fixed power density of 1.41 GW/cm2. By maintaining a consistent power density through laser energy compensation, the influence of the incidence angle on surface integrity and wear resistance of the hole structure was systematically investigated. The results show that as the impact angle increases from 0° to 45°, the depth of the affected material layer gradually decreases. Surface microhardness and residual compressive stress peak at a 30° impact angle, reaching values of 633.5 HV1 and 517.4 Mpa, respectively. Wear tests indicated that the friction coefficient was lowest at 30° (0.542), with the dominant wear mechanism shifting from abrasive to adhesive wear. Under controlled power density conditions, oblique laser impact improves surface properties at the expense of a reduced thickness of the affected layer.