Non-Destructive Evaluation and Characterization of Transparent MgAl2O4 Spinel Ceramics via Moiré Interferometry

This work employs moiré interferometry to investigate the influence of sintering temperature and sandblasting on the optical and mechanical properties of magnesium aluminate spinel (MgAl2O4). S25CRX14 Spinel pellets were fabricated via Spark Plasma Sintering (SPS) at 1300 °C, 1350 °C, and 1400 °C. The sintered samples were subsequently analyzed before and after sandblasting. Moiré interferometry, a non-destructive and contactless technique based on the superposition of tow linear transmission gratings, has proven particularly suitable for detecting micro-defects in transparent materials. The analysis of moiré fringes provided essential insights into the presence and size of defects, enabling accurate quality assessment without altering the samples. Its high spatial resolution, allowed the detection of even low-contrast defects. The results confirmed that the sintering temperature and sandblasting significantly influenced the mechanical and optical properties of the S25CRX14 spinel samples. The specimens sintered at 1350 °C exhibited the highest light transmission and the superior hardness. In contrast, the samples sintered at 1400 °C showed a notable degradation in their optical and mechanical properties. In conclusion, the pellets sintered at 1350 °C demonstrated the most favorable overall performance. This study confirms that moiré interferometry is a straightforward, accurate, and highly effective method for evaluating transparent ceramics, with very low implementation costs.