Hierarchically Porous Nitrogen‐Doped Carbon with High Conductivity for Rapid and Efficient Cr(VI) Reduction

Carbon‐based materials derived from metal–organic frameworks typically exhibit microporous structures and low conductivity, which significantly limit their catalytic activity. Herein, an effective strategy to prepare dodecahedral hierarchical porous nitrogen‐doped carbon‐based composites (d‐PNC) by using ZIF‐8 encapsulated with ionic liquid as pyrolysis precursors for efficient Cr(VI) reduction is developed. The encapsulated ionic liquid helps to precisely regulate the hierarchically porous structure in d‐PNC. This hierarchically porous structure not only creates a favorable reaction microenvironment, facilitating the mass transfer of Cr species and their interaction with active sites, but also enhancing the conductivity of d‐PNC and consequently accelerating the electron transfer of •CO 2 − radicals to Cr species, thereby speeding up the reduction process of Cr(VI). Additionally, with the calcination temperature increasing, the content of defective C increases, and N species progressively transforms into graphitic‐center N (N3). Density functional theory calculations reveal that the defective C active center substantially decreases the free energy change of the rate‐determining step (from Cr(IV) to Cr(III)) through the synergistic effect of N3. Given these outstanding characteristics, the optimized d‐PNC material can completely reduce Cr(VI) (333.3 mg g −1 ) in an oxalic acid solution within 2 min, outperforming its counterparts without a hierarchical structure and those calcined at significantly lower temperatures.