The Role of Rotational Tool Speed in the Joint Performance of AA2024-T4 Friction Stir Spot Welds at a Short 3-Second Dwell Time

This study explores Friction Stir Spot Welding (FSSW), a well-established solid-state joining technique, for high-strength aluminum alloys like AA2024-T4, which present significant challenges for conventional welding techniques. This research focuses on the impact of relatively low rotational speeds, specifically within a range of 700 to 1300 rpm, on the mechanical and microstructural properties of the welded joints. By employing a short dwell time of 3 s, this study aims to enhance productivity in the automotive and aerospace industries. The experimental work evaluated the joints’ thermal cycles, macrostructure, microstructure, hardness and load-carrying capacity. Results indicated a linear relationship between rotational speed and heat input. Although all welds exhibited a significant grain size reduction in the stir zone (SZ) compared to the base material (29.7 ± 6.1 μm), the SZ grain size increased with rotational speed, ranging from 4.7 ± 1.4 to 8.3 ± 1.3 μm. This study identified 900 rpm as the optimal parameter, achieving the highest load-carrying capacity (7.35 ± 0.4 kN) and a high SZ hardness (99 ± 1.5 HV). These findings confirm that joint strength is a balance between grain refinement and thermal softening. The presence of precipitates and the fractography of the tensile–shear tested specimens were also investigated and discussed.