Non-Ferrous Metal Bioleaching from Pyrometallurgical Copper Slag Using Spent Medium of Different Fungal Species

Copper slag, a by-product of copper ore and concentrate smelting, is rich in non-ferrous metals; therefore, it has been considered a valuable raw material in recent years. This study aimed to compare the extraction of zinc, copper, and cobalt from two types of copper slag from a dump located near the village of Eliseyna, Bulgaria, which differ in mineralogical composition and chemical content, using indirect bioleaching with a spent medium of Aspergillus niger and Penicillium ochrochloron. Chemical leaching with sulphuric acid revealed that zinc and cobalt existed mainly as an acidic-soluble phase in both types of copper slag. In contrast, it contained 50–75% of the total copper content. Each fungal species was cultivated for one week, and the biomass and the spent medium were separated a week later. Owing to the production of a higher concentration of citric acid, A. niger facilitated more efficient base metal recovery. However, their effective recovery from the acidic-soluble phase required leaching at a 5% pulp density and supplementing the spent medium with sulphuric acid. The temperature played a secondary role. Conclusions: Non-ferrous metal extraction from copper slag exposed to weathering using a spent medium supplemented with sulphuric acid was achieved under milder leaching conditions and with better selectivity. In contrast, slag unaffected by weathering behaved as a refractory due to the worsened results of base metal extraction under similar experimental conditions.