Enhancement of Cutting Performance of Ceramic Tools by Addition of Exogenous Precursor Restorers

To address brittle cracks in ceramic tools, an exogenous precursor ceramic repair agent was developed and applied to Al2O3/TiC/NiMo composite ceramic tools, which were treated by a two-step heat treatment process (heating at 3 °C/min to 300 °C for 60 min, heating the sample at 5 °C/min to 500, 600, 700, 800, and 900 °C, holding each for 60 min). The crack healing mechanism and temperature dependency of the repair agent were investigated. Cutting performance, including surface roughness, cutting force, and tool life, was optimized using an L9(34) orthogonal design. The results show that at 900 °C, the repair agent decomposed to form SiOC (Silicon Oxycarbide) amorphous phase and TiB2 reinforced phase, filling the cracks and achieving atomic-level diffusion bonding. The flexural strength of the repaired sample recovered to 79.9% of the initial value (456.5 MPa), a 196.4% increase compared to the unrepaired sample. Optimal cutting parameters were found to be a cutting speed of 200 m/min, back draft of 0.1 mm, and feed of 0.1 mm/r. Under these conditions, surface roughness was 0.845 μm, cutting temperature was 258 °C, and stable tangential force was 70 N. The effective cutting distance of the repaired tool was increased from 1300 m to 1700 m. Wear was primarily abrasive and adhesive wear, and the SiOC phase formed by the repair agent helped to fill and repair the flank, thus extending tool life.