Research on Arc Characteristics and Microstructure of 6061 Aluminum Alloy Multi-Pulse Composite Arc Welding

To mitigate welding defects and optimize the microstructure of aluminum alloys, this study introduces a multi-pulse hybrid arc welding process. A comparative investigation was carried out between this novel process (AC/DC composite 1 kHz pulsed welding) and conventional methods (AC pulsed, AC/DC pulsed) during wire-fed overlay welding of 6061 aluminum alloy. Analyses were conducted on electrical signals, arc morphology, joint microstructure, and hardness. The results indicate that the AC/DC hybrid 1 kHz pulsed process combines the characteristics of both AC and DC pulsed signals with full-cross-section frequency pulse superposition, thereby optimizing arc welding process control. The frequency pulses induce a magnetoelectric effect, leading to significant arc constriction, which enhances arc energy density and arc pressure. This intensifies the fluid flow in the molten pool and accelerates cooling, thereby suppressing the growth of columnar grains and promoting the formation of fine equiaxed grains and an increased proportion of high-angle grain boundaries. Meanwhile, this process effectively reduces the number, area fraction, and overall porosity, and facilitates the distribution of a large amount of Al–Si eutectic structure along grain boundaries, enhancing the impediment to dislocation motion. The microstructural optimization significantly improves the hardness at the weld center to 73.1 HV, leading to enhanced mechanical properties.