The Impact of Ce on the Microstructure and Properties of Weld Metal in Corrosion-Resistant Steel

In this study, two types of submerged arc welding (SAW) wires were prepared—one without cerium (Ce) and another containing 0.14 wt.% Ce. Deposition experiments were carried out on corrosion-resistant crude oil storage tank steel plates using a multi-layer, multi-pass welding process. Through a combination of microstructural characterization techniques, including optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM), along with mechanical property testing, a systematic investigation was conducted to evaluate the influence of Ce on the weld metal microstructure and its impact toughness at −20 °C. The results reveal that Ce introduced via the welding wire into the weld seam refines and disperses inclusions, leading to the formation of composite inclusions primarily composed of Ce2O3, Ce2O2S, and CeS. These Ce-enriched inclusions serve as heterogeneous nucleation sites, increasing the area fraction of acicular ferrite (AF) within the weld columnar grain region from 52% to 83%, and within the heat-affected zone from 20% to 37%. Correspondingly, the proportions of blocky and polygonal ferrite decrease, while the size of martensite/austenite (M/A) constituents is reduced. The addition of Ce thus diminishes the size of hard phase inclusions and M/A constituents in the weld metal, enhancing the critical fracture stress and increasing the energy required for crack initiation. Meanwhile, the higher proportion of AF elevates the density of high-angle grain boundaries, thereby improving crack propagation resistance. These combined effects raise the −20 °C impact energy of the weld metal from 117 J to 197 J.