Green Synthesis of Activated Carbon from Waste Biomass for Biodiesel Dry Wash

The valorization of agro-industrial waste could be a strategy to improve organic waste management. The production of activated carbon (AC) is a path to use for this waste, with the aim of reducing its negative effects. AC is characterized by a high internal surface area, chemical stability, and oxygen-containing functional groups in its structure. This work is focused on the valorization of agro-industrial waste such as pineapple peel and coconut shells. These are made up of sucrose, glucose, fructose, and other essential nutrients, as well as cellulose, hemicellulose, and lignin. Activated Carbon was obtained with slow pyrolysis at 400 °C, for 4 h in a stainless-steel tubular reactor with physical activation. The obtained samples were analyzed using SEM, TGA, FTIR, and BET to verify the morphology, thermal degradation, functional groups and pores ratio of the AC, highlighting the presence of materials pore >10 µm. The TGA residual materials gave 16.3% of pineapple peel AC ashes and 0.2% of coconut AC. A C=C, C-HX, CO, and OH stretching were observed in 400–4000 cm−1. The peak intensity decreased once the biodiesel was treated with AC, because the traces of water and functional groups interacted actively, resulting a high content of bases. Activated carbon was used for dry cleaning of the obtained biodiesel from residual oil, which was effective in reducing pH and moisture levels in the biodiesel samples. Pore distribution was determined by BET, 5.6 nm for pineapple peel and 39.8243 nm for coconut shells. The obtained activated carbon offers a sustainable alternative to traditional carbon sources and contributes to the circular economy by recycling waste biomass.