To achieve the resource utilization of solid waste generated from the papermaking process, this study proposes a method for preparing sintered bricks by partially replacing shale with paper-mill sludge. The brick samples were prepared through a process of mixing in proportion, extrusion molding, drying and roasting. An orthogonal experimental design was employed to investigate the effects of sintering temperature, raw material proportion, and holding time on the physical and mechanical properties of the bricks. The results indicate that the optimal technological parameters are determined as follows: a raw material proportion (paper-mill sludge:shale) of 30:70, a sintering temperature of 1050 °C, a holding time of 8 h, and a heating rate of 1 °C/min. Under these conditions, the produced paper-mill sludge–shale bricks exhibited a compressive strength of 14.91 MPa, a flexural strength of 8.26 MPa, a water absorption of 12.7%, and a bulk density of 1712 kg/m3. These performance indicators meet the requirements for Grade MU10 specified in the national standard Sintered Common Bricks (GB/T 5101-2017). Regarding microscopic analysis, the SEM results reveal significant liquid-phase sintering within the brick body at 1050 °C, while XRD analysis confirmed the presence of stable quartz, alumina, and hematite phases, which contribute to enhancing the mechanical properties and densification of the bricks.
Meng et al. (Mon,) studied this question.