A Novel Energy-Based Crack Resistance Assessment Method for Steel Fiber-Reinforced Lightweight Aggregate Concrete via Partially Restrained Ring Tests

Early-age cracking limits the structural use of steel fiber-reinforced lightweight aggregate concrete (SFLWAC), and robust experimental evaluation methods are still needed. This study examines the influence of steel fiber volume fractions (i.e., 0%, 0.5%, 1.0%, and 2.0%) on the cracking performance of SFLWAC through mechanical testing, autogenous shrinkage measurements, and two types of partially restrained ring tests, with and without a clapboard. The performance of three crack resistance indices is compared: the strain-based ASTM C1581 index, a stress-based area index, and a newly proposed energy-based index defined as the strain energy accumulation degree (SEAD), i.e., the ratio between the accumulated and critical strain energy density. The 28-day splitting tensile strength was improved by 77.9% and autogenous shrinkage was diminished by 30.7% as steel fiber volume content increased from 0 to 2.0%, thereby improving the resistance to shrinkage-induced cracking. In the partially restrained ring tests, SEAD decreased with increasing fiber content, and crack initiation occurred when SEAD reached an approximately constant threshold, whereas ASTM C1581 and the area index could not consistently rank mixtures when some rings cracked and others remained intact. These results demonstrate that SEAD provides a physically meaningful and unified measure of cracking risk for SFLWAC under partially restrained shrinkage and has the potential to be extended to other fiber-reinforced concretes and shrinkage-related cracking problems.