To investigate the hot deformation characteristics of the Al–10Mg–3Zn alloy, a series of hot compression tests was carried out using a Gleeble-3500 simulator. The experimental matrix covered temperatures of 300–450 °C and strain rates from 0.001 to 10 s−1. The true stress–strain curves were obtained and the hot processing map of the alloy was constructed based on the Dynamic Material Model principle. The multi-objective optimization of the extrusion process parameters was performed using the response surface method. The results showed that the flow stress of Al–10Mg–3Zn alloy increased with the increase in the strain rate and decreased with the increase in the deformation temperature, indicating that the alloy had a positive strain rate sensitivity. A strain-compensated Arrhenius constitutive model and a hot processing map of Al–10Mg–3Zn alloy were established based on the temperature-corrected data; here, the optimal temperature range and strain rate range for hot processing were specified. The optimal extrusion process parameters, determined by the response surface method, were as follows: billet temperature of 400 °C, extrusion speed of 0.20 mm/s, and ingot length of 350 mm. With this parameter combination, the simulation predicted an extrusion load of 73.29 MN, a velocity deviation of 24.96%, and a cross-sectional temperature difference of 9.48 °C for the profile. The predicted values from the response surface method were highly consistent with those from the finite element simulation. The optimized process parameters significantly reduced the extrusion load of the profile.
Niu et al. (Sat,) studied this question.