Mechanistic Insights into Asphalt Natural Aging: Microstructural and Micromechanical Transformations Under Diverse Climates

Understanding mechanisms of asphalt in the process of natural aging is crucial for predicting its long-term durability and optimizing performance under diverse environmental conditions. Despite its importance, the microstructural and micromechanical changes induced by natural aging remain poorly understood, particularly under varying climatic influences. This study addresses this gap by analyzing the effects of natural aging on asphalt’s microscopic properties and identifying key indicators that govern its degradation. Asphalt samples were subjected to natural aging across five climatically distinct regions over 6, 12, and 18 months. Atomic force microscopy (AFM) was employed to characterize surface roughness, adhesion forces, and DMT modulus, while correlation analysis and principal component analysis (PCA) were used to identify relationships among micromechanical indicators and streamline the dataset. The results reveal that natural aging induces irreversible transformations in asphalt’s microstructure, driven by the combined effects of temperature, UV radiation, humidity, and oxygen. These processes promote the evolution of “Bee structures,” increase surface roughness, and accelerate phase separation, alongside chemical modifications such as oxidation and polymerization, leading to progressive material hardening and stiffness. Significant regional and temporal variations in adhesion forces and DMT modulus were observed, reflecting the cumulative impact of environmental factors on asphalt’s aging dynamics. Correlation analysis demonstrated strong associations between surface roughness and “Bee structure” area, while mechanical properties such as stiffness and adhesion were largely decoupled from morphological features. Environmental factors interact in complex ways to drive asphalt aging. Humidity enhances adhesion and stiffness via water-induced capillary forces, while temperature reduces surface roughness and adhesion through molecular reorganization. UV radiation accelerates oxidative degradation, promoting surface erosion and stiffness loss, while altitude modulates these dynamics by influencing temperature and UV exposure.