Developing low-carbon building materials is essential for achieving sustainability in the construction sector. This study proposes a carbon-negative concrete (CNC) system that combines low-carbon binders derived from industrial by-products with carbonated recycled aggregates capable of CO2 absorption. To enhance particle packing and mechanical performance, the Modified Andreasen–Andersen (MAA) model was adopted for mix design optimization and experimentally validated. The optimized CNC mixture containing 22% coarse aggregate achieved the minimum residual sum of squares between the graded particle distribution and the theoretical MAA curve, as well as the highest strength performance. Compared with a 14% coarse aggregate mixture, the 22% mix exhibited 13.5% and 19.8% increases in compressive strength at 7 and 28 days, confirming the applicability of the MAA model for CNC proportioning. Carbon emission assessment, limited to raw material production, demonstrated significant environmental benefits. CNC incorporating both low-carbon binders and carbonated recycled aggregates reduced total emissions and CO2 intensity by 87.1% and 86.2%, respectively, compared with ordinary concrete of the same strength grade. Economic evaluation further showed that CNC reduced material cost by 48.1% relative to ordinary concrete. It should be emphasized that the reported CO2 reduction and negative emission effects are limited to the defined raw material production boundary and do not represent a fully net-negative life cycle. Overall, these results confirm the technical, environmental, and economic feasibility of CNC as a sustainable alternative to traditional concrete.
Lin et al. (Thu,) studied this question.