Cocontinuous polymeric nanomaterials have gained attention for their ability to preserve distinct properties of constituent microphases within a single material. Randomly linked copolymer networks have shown very wide stability windows for disordered cocontinuous phases (extending over ≈ 30 wt % in composition), but the reliance on a network architecture prevents subsequent solution- or melt-processing. Furthermore, the key factors contributing to cocontinuity have remained unclear. We recently found that randomly linked star copolymers (RSCs) can exhibit a cocontinuous window as wide as 25 wt % in the case of 4-arm stars, suggesting that while a network architecture is not essential for the formation of disordered cocontinuous phases, the presence of random elastic forces in such architectures may indeed facilitate their formation. In addition, the behavior was found to be highly sensitive to arm number, with 6-arm RSCs exhibiting almost no cocontinuous phase. These results raised a key mechanistic question regarding the contribution of random elastic forces, originating from strands that bridge between junctions, in stabilizing disordered cocontinuous phases. In the current study, we synthesized randomly linked branched copolymers (RBCs) of polystyrene (PS) and poly(D,L-lactic acid) (PLA), which represent an intermediate architecture between networks and stars. This approach allows for the introduction of elastic contributions from strands bridging between different junctions, while still maintaining the processability advantages of a non-network architecture. The cocontinuous regions of the PS/PLA RBCs, with varying polymer and linker functionalities (fp and fl, respectively), were characterized by small-angle X-ray scattering, gravimetry, and scanning electron microscopy. We found that the cocontinuous windows of RBCs typically expanded with increasing elastic contributions and exhibited reduced sensitivity to junction-functionality compared to RSCs. Notably, RBCs with fp = 1.50 and fl = 3, which had large molecular weights due to proximity to the gel point, achieved a cocontinuous window of ≈ 34 wt %, which is almost twice as wide as analogous 3-arm RSCs and comparable to randomly linked networks. Leveraging this robust cocontinuity and solution-processability, we fabricated a film of interconnected nanoporous PS.
Ju et al. (Thu,) studied this question.