Texture development in magnetostrictive Fe-Ga alloys processed by laser powder bed fusion

• Near full-density Fe-Ga alloy parts were fabricated using laser powder bed fusion (LPBF). • Record-high saturation magnetostriction of 190 ppm was achieved in as-printed material due to strong fiber texture by combination of high laser power and slow scan speed. • EBSD-based texture analysis enabled estimation of intrinsic magnetostriction constants. Iron-gallium (Fe-Ga, Galfenol) alloys are promising magnetostrictive materials for actuators, sensors, and energy harvesting, but their performance is highly sensitive to microstructure and texture. Additive manufacturing by laser powder bed fusion (LPBF) offers a pathway to engineer texture and integrate functional materials into complex geometries. Here, we fabricate Fe-Ga alloys (Fe 82.2 Ga 17.8 ) by LPBF of gas-atomized powders and systematically optimize laser power and scan speed to maximize density and control texture. Nearly full-density parts (up to 99.6 %) are achieved within a narrow processing window. Electron backscatter diffraction (EBSD) reveals a strong <100> fiber texture aligned with the build direction and columnar grains up to 1 mm long. Magnetostriction measurements show saturation magnetostriction of 190 ppm in the build direction. Correlating texture data with macroscopic magnetostriction, we estimate intrinsic magnetostriction constants (λ 100 = 228 ppm, λ 111 = 12 ppm), closely matching single crystal-derived values. These results demonstrate the critical interplay between processing, texture, and functional performance in additively manufactured Fe-Ga alloys and establish LPBF as a viable route for high-performance magnetostrictive materials.