Injection-molding purges are heterogeneous, bulky residues whose uncertain composition and irregular geometry hinder direct reinsertion, making cold shredding costly and maintenance-intensive. This work develops a low-infrastructure solar-assisted pre-processing route using a PMMA Fresnel lens to induce controlled sub-onset softening and enable clean shear cutting without destructive thermal histories. The sub-onset softening is here defined into a viscoelastically active range (at or above Tg for the amorphous phase) while remaining below the melting onset (Tm, onset) and below the onset of thermal degradation (Td, onset). The station was engineered via QFD and risk-oriented design tools, while a weighted Pugh matrix selected shear cutting over saw-based alternatives. A screening factorial DOE showed that lens height, angle, and their interaction significantly govern focal-spot diameter and receiver temperature, yielding linear relations for conservative set-point selection. Receiver benchmarking further indicated that copper reaches substantially higher temperatures than graphite under identical exposure conditions, supporting copper as the simplest, rapid-heating receiver. Under DOE-calibrated operation, tear-free shear cutting was achieved across representative purge families (PP–ABS, PC–ABS–PP, PA66, PA66-filler, and POM) without forced convection. From a recycling and waste-management perspective, the approach converts bulky purge scrap into mill-compatible feedstock with reduced mechanical resistance, lowering tool wear and fines generation, accelerating downsizing, and limiting stockpiling that elevates combustible-inventory fire risk. Overall, the proposed DOE-calibrated, operator-friendly framework improves recycling feasibility by enabling safer handling, more stable preprocessing throughput, and reduced reliance on disposal or long-term storage for heterogeneous industrial purges.
Plaza et al. (Thu,) studied this question.