Antimony oxide nanoparticles (Sb2O3 NPs) were synthesized via a chemical vapor deposition (CVD) method and systematically characterized to evaluate their multifunctional performance. Powder X-ray diffraction (PXRD) confirmed the formation of an orthorhombic Sb2O3 phase with an average crystallite size of 53.50 nm, while SEM analysis revealed elongated nanostructures with diameters in the range of 20–100 nm. The stoichiometric composition of Sb2O3 (Sb:O ≈ 2:3) was verified by EDAX, and optical studies indicated a direct band gap of 3.10 eV. The electrochemical sensing capability of Sb2O3 NPs was investigated using a modified nickel mesh electrode for the detection of Metronidazole (MTZ) in 0.1 N KOH. The presence of Sb2O3 NPs resulted in an additional irreversible reduction peak at −0.14 V, confirming enhanced electrocatalytic activity toward MTZ, along with excellent cycling stability (94.36% retention after 10 cycles). In addition, the photocatalytic performance of Sb2O3 NPs was evaluated through the degradation of Acid Orange (AO) dye under UV-Vis irradiation, achieving a degradation efficiency of 73.31%. These results demonstrate that Sb2O3 nanoparticles are promising multifunctional materials for environmental remediation and electrochemical sensing applications, highlighting their potential for industrial implementation.
Khasim et al. (Wed,) studied this question.