Biodegradable nanocomposite materials possessing self-healing behavior are emerging as an attractive option of being used in advanced mechatronic systems. The current study is focused on a thorough examination of the micromechanical properties of graphene–reinforced polylactic acid (PLA)/polycaprolactone (PCL) composite samples, followed by estimation of their self-healing behavior upon heating. Polymer blend–based nanocomposite materials were prepared using the green and reliable in terms of good nanofiller dispersion melt extrusion method. 3D printed nanocomposite specimens with impeccable flatness were subjected to fine microscratch testing by applying a constant force experimental mode. The surface resistance of the three-component polymer materials against the lateral movement of the stylus fulfilling the scratch and the impact of the dual-phase PLA/PCL ratio on the nanocomposite mechanical performance were estimated by calculation of the coefficient of friction (COF = Fx/Fz). COF values in the range of 0.8–1.4 indicated excellent nanocomposite resilience against scratch. Creating a heterogeneous polymer system that combines phase-separated soft and hard domains with close melt and glass transition temperatures, respectively, may facilitate the physical flow of macromolecular chains into voids or free volume areas. This aspect can be critical in the achievement of thermally–induced self-healing properties of the composite material. Scanning electron microscopy (SEM) imaging of the microscratches, made before and after Joule heating of the polymer samples, revealed a significant degree of surface recovery and a sensible reduction in the width of the adjusted scratch grooves.
Batakliev et al. (Tue,) studied this question.