Electro-carburization of mild steel through two-step reaction in molten-salt electrolyte

The rapid carburization of mild steel is demonstrated via the electrochemical deposition of solid carbon, followed by thermochemical iron-carbon (Fe-C) reaction using a molten lithium-potassium carbonate (LiKCO3) salt electrolyte and carbon dioxide as the carbon source. Depth-dependent microstructural and compositional changes in the steel are shown to be controlled by the applied cell voltage and reaction temperatures. Reaction temperatures above the Fe-C eutectoid temperature promote faster carburization due to carbon dissolution into austenite. The carbon deposition rate is regulated by the applied cell voltage: At − 2.4 V, carbon deposition occurs much faster than its diffusion into the steel, resulting in the accumulation of a carbon-rich layer exceeding 1 mm, which does not diffuse into the steel. In contrast, at − 1.8 V, all deposited carbon effectively diffuses into the steel, leaving a minimal external deposit. In both cases, carbon ingress forms a carbide-rich surface layer and precipitates additional carbides along the grain boundaries within the steel electrode. This method offers a potential approach to increase the carbon content of mild or low-carbon steel feedstocks, such as scrap or direct reduced iron, for industrial applications.