Structural, Barrier, and Mechanical Enhancement of Pectin–Alginate Biocomposite Films Reinforced with Alkali-Treated Rice-Husk Fiber

In this study, rice-husk fiber (RHF) extracted via alkali hydrolysis was used as a reinforcing material (0–10 wt%) in a pectin-sodium alginate (PE/SA) matrix to develop biofilms by the casting method. These biofilms were characterized by using FTIR, XRD, TGA, and DSC. The thickness, moisture content, water solubility, swelling behavior, water-contact angle, water-vapor permeability, optical transparency, and mechanical properties of biofilms were investigated. It was observed that the PE/SA/RHF film loaded with 5% RHF had better visual attributes, and a further increase in reinforcement was not found to be as favorable. The addition of 10 wt% RHF significantly enhanced the thickness from 0.094 to 0.127 mm, water solubility from 49.25 to 56.13%, water-contact angle from 48.4 to 62.6°, and tensile strength from 4.17 to 10.23 MPa. However, decreases in water-vapor permeability from 1.94 × 10−9 to 1.32 × 10−9 g·m−1·Pa−1·s−1 and in elongation at break from 19.24 to 2.87% were observed in the biofilms. Structurally, FTIR confirmed intermolecular hydrogen bonding between components. XRD revealed that the films remained predominantly amorphous, without significant crystalline alterations. Furthermore, thermal stability improved with the addition of RHF. Finally, these PE/SA/RHF composite films may be potential eco-friendly biodegradable packaging candidates for food industry applications.