Comparative thermodynamic analysis identifies optimal oxygen carriers for hydrogen production, suggesting efficiency in chemical looping reforming processes.
A comparative thermodynamic analysis of the three-stage CLRWS process (methane reforming, water splitting, and air reoxidation) was performed for iron-based oxygen carriers, including Fe2O3 supported on SiO2, TiO2, MgO, MgAl2O4, and YSZ, alongside the self-supported SrFe12O19. While CH4 conversion and syngas yield were similar, carbon deposition varied significantly, being lowest for SrFe12O19 and Fe2O3/MgAl2O4. Stable phase formation (Fe2SiO4, FeTiO3) on SiO2 and TiO2 limited reduction depth and oxygen availability. SrFe12O19 exhibited the highest metallic iron content, enabling a hydrogen yield of 10.6 mmol/g at >98% purity. Carriers with inert supports (YSZ, MgAl2O4) exhibited classical oxidation, while others formed mixed oxides that could hinder regeneration. All systems required external heat, with the highest demand for YSZ-, MgAl2O4-, and SrFe12O19-based carriers. Steam input variation enabled hydrogen output control and potential autothermal operation. Overall, Fe2O3/MgAl2O4 and SrFe12O19 showed the best potential for CLRWS, combining low carbon deposition, high reversibility, and thermal flexibility.
No takes yet. Share an insight, caveat, or question.
Shamsutov et al. (2026) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: