Comparative Study on Photothermal Adaptive Performance of Phase-Change Photovoltaic Window in Summer Conditions

This study integrates phase change material (PCM) with semi-transparent photovoltaic (PV) glazing to develop a composite window providing thermal buffering and PV temperature regulation in summer. A PCM-PV double glazing window (PCM-PV-DGW) using paraffin PCM and CdTe semi-transparent PV glass was fabricated and evaluated through outdoor hot-box experiments and transient modeling in Qingdao, China. Four window types—DGW, PCM-DGW, PV-DGW, and PCM-PV-DGW—were tested under identical boundary conditions. The coupled system showed improved photothermal performance, achieving a daily average Solar Heat Gain Coefficient (SHGC) of 0.105, compared with 0.180 for PV-DGW without PCM filling, together with a temperature attenuation factor of 0.904 and a 35 min peak temperature delay. A two-dimensional transient heat transfer model incorporating radiative transfer through semi-transparent layers and an enthalpy-based phase change method was established and validated against measured inner-surface temperatures, showing good agreement (RMSE 1.54–1.80 °C). Parametric and sensitivity analyses indicate that PCM phase transition temperature is the dominant parameter (suggested 28–32 °C), while ~12 mm PCM thickness and 50% PV coverage offer a practical balance for the Qingdao summer scenario. The results provide preliminary guidance for PCM–PV window design under the investigated summer conditions.