Experimental study shows that ultrafine-grained state enhances wear resistance in AMg6 alloy under sliding friction.
The effect of the structural state of a deformable aluminum alloy on its wear resistance under high sliding speed conditions has been experimentally studied. Equal-channel angular pressing method was used to form different structural states in the AMg6 alloy. The formation of an ultrafine-grained state of the samples was established using transmission electron microscopy. It was found that a change in the structure made it possible to increase the mechanical properties under tension and the nanohardness of the AMg6 alloy. To study the tribological properties, tests were performed under dry friction conditions with different sliding speeds. The ultrafine-grained state was experimentally established to contribute to a decrease in the friction coefficient. The sliding speed and structural state affect the wear intensity of the studied samples. It is shown that triboxidation of the sample surface is a mechanism for increasing the wear resistance of the AMg6 alloy. It has been found that the sliding speed affects the formation of the surface layer and deformation in the near-surface zone in the studied samples. Oscillations of the tribological system have been studied by analyzing the vibration amplitude. It has been established that the formation of the ultrafine-grained structure helps to reduce oscillations in the tribological system. The change in the parameters of acoustic emission signals depending on the sliding speed and structural state of the samples has been studied. A correlation has been revealed between wear indicators and dynamic characteristics of the tribosystem.
No takes yet. Share an insight, caveat, or question.
A.V. Filippov (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: