Effect of Glass Fibers on the Mechanical and Transport Properties of Polymer Inclusion Membranes Composed of Aliquat 336 and PVDF-HFP

Polymer inclusion membranes (PIMs) based on PVDF-HFP as the base polymer and Aliquat 336 as the carrier in a mass ratio of 6:4 with concentrations of embedded glass fibers up to 5 wt% were successfully fabricated. Their microstructure, as well as their mechanical and thermal properties, were characterized using scanning electron microscopy (SEM), small-angle X-ray scattering (SAXS), differential thermal analysis/thermogravimetric analysis (DTA/TGA), and tensile testing. Membrane performance and long-term stability in transporting thiocyanate ions were evaluated in a two-compartment transport cell. The results showed that the membranes retained their amorphous structure even with glass-fiber loadings of up to 5 wt%. The addition of glass fibers was found to primarily enhance the elastic modulus and tensile strength, while causing a moderate reduction in plasticity without negatively affecting membrane transport properties and long-term stability. Therefore, it was concluded that the incorporation of glass fibers could improve the suitability of PIMs for industrial applications.