This study investigates the fracture initiation and propagation mechanisms of continuously reinforced concrete–asphalt (CRC+AC) composite pavements under the synergistic effects of diurnal temperature fluctuations and non-uniform tire loading. A three-dimensional (3D) thermo-mechanical coupled finite element (FE) model was developed, with its underlying mechanical framework validated through laboratory-scale model tests conducted at 20 °C. The experimental results, involving strain monitoring at varying depths, demonstrated a high degree of consistency with numerical predictions in terms of spatial strain distribution, thereby ensuring the model’s reliability in capturing interlayer load-transfer efficiency. Building upon this validated mechanical foundation, numerical simulations were extended to analyze the low-temperature fracture response. The numerical results indicate that the maximum longitudinal and transverse tensile stresses in the asphalt layer are concentrated at the pavement surface, whereas the maximum shear stress occurs at a depth of 2–3 cm near the leading and trailing edges of the wheel load. Under low-temperature gradients, the Mode I stress intensity factor (KI) at the crack tip exhibits a distinct diurnal opening–closing–reopening pattern, peaking at approximately 220 kPa·m1/2 during the early morning hours (05:00–06:00). Furthermore, numerical simulations reveal the significant sensitivity of shear-sliding to axle loads; specifically, the peak Mode II stress intensity factor (KII) increases monotonically from 190 to 230 kPa·m1/2 as the axle load rises from 10 t to 16 t. Under non-uniform contact pressure, longitudinal cracking is primarily characterized by a mixed Mode I and Mode II mechanism driven by coupled tensile and shear stresses, whereas transverse cracking is dominated by Mode II shear failure. These findings suggest that implementing targeted traffic restrictions for overloaded vehicles during identified high-risk time windows can significantly enhance the structural durability and service life of composite pavements in cold regions.
Xu et al. (Sat,) studied this question.