Liquid Crystalline Perylene Bisimide Derivatives Bearing Oligosiloxane Moieties

Perylene bisimide derivatives are typical n-type semiconductors as well as redox-active materials. However, it has been difficult to produce thin films by solution processes because of their low solubilities in organic solvents. Perylene bisimide derivatives bearing oligosiloxane moieties exhibit columnar phases over wide temperature ranges, including room temperature and high solubilities in organic solvents. The columnar phases are stabilized by nanosegregation between crystal-like one-dimensional π-stacks and liquid-like mantle consisting of oligosiloxane moieties. The electron mobility at room temperature exceeded 0.1 cm2V−1s−1 in the ordered columnar phases of perylene bisimide derivatives bearing four disiloxane chains. Uniaxially aligned thin films of the perylene bisimide derivatives bearing oligosiloxane moieties could be produced by a spin-coating method. The spin-coated films of the perylene bisimide derivatives bearing cyclotetrasiloxane rings could be insolubilized via in situ ring-opening polymerization by the exposure of the thin films to trifluoromethanesulfonic acid vapors. Uniaxially aligned thin films of perylene bisimide derivatives bearing an ethylene oxide chain as well as cyclotetrasiloxane rings could be doped in an aqueous solution of sodium dithionate, resulting in an anisotropic electrical conductivity. Polymerized thin films of perylene bisimide derivatives bearing a crown ether ring exhibited electrochromism in electrolyte solutions. These compounds formed 1:1 complexes with lithium triflate, exhibiting columnar phases at room temperature. The nanostructures of the complexes were stabilized by the electrostatic interaction between cationic crown-metal units and triflate anions.