Effect of scanning strategy on texture formation in Ni-25 at.%Mo alloys fabricated by selective laser melting

• Fabrication of Ni-25 at.%Mo product was succeeded by the selective laser melting. • Texture development can be controlled by changing the scanning strategy of the laser. • Aligned crystal orientation along the build direction can be varied in 〈001〉 or 〈101〉. • Controlling mechanism of the texture was clarified by microstructure observation. Variations in the crystallographic texture in Ni-25 at.%Mo alloys fabricated by selective laser melting with different scanning strategies were designed for the first time. Single-crystalline-like texture with a short-range order of Mo atoms can be produced via bidirectional scanning along one axis (X-scan) and bidirectional scanning with a 90° rotation in each layer (XY-scan), while only fiber texture was formed in bidirectional scanning with a 67° rotation (Rot-scan). The aligned crystal orientation along the build direction can be varied by the scanning strategy; 〈001〉 is preferred in the XY- and Rot-scan samples, while 〈101〉 is preferred in the X-scan sample. The controlling mechanisms of the texture, focusing on the preferential growth directions of the columnar cells and the following epitaxial growth, are discussed.