The Roles of Structural Imperfections in InGaN-Based Blue Light-Emitting Diodes and Laser Diodes

REVIEW High-efficiency light-emitting diodes emitting amber, green, blue, and ultraviolet light have been obtained through the use of an InGaN active layer instead of a GaN active layer. The localized energy states caused by In composition fluctuation in the InGaN active layer are related to the high efficiency of the InGaN-based emitting devices. The blue and green InGaN quantum-well structure light-emitting diodes with luminous efficiencies of 5 and 30 lumens per watt, respectively, can be made despite the large number of threading dislocations (1 x 10(8) to 1 x 10(12) cm-2). Epitaxially laterally overgrown GaN on sapphire reduces the number of threading dislocations originating from the interface of the GaN epilayer with the sapphire substrate. InGaN multi-quantum-well structure laser diodes formed on the GaN layer above the SiO2 mask area can have a lifetime of more than 10,000 hours. Dislocations increase the threshold current density of the laser diodes.