Effect of Ta on Microstructure, Mechanical Properties, and Soft Magnetic Performance of Fe-Based Amorphous Coatings Prepared by High-Speed Laser Cladding

High-speed laser cladding (HLC) technology can provide high cooling rates and low dilution rates for the preparation of metastable Fe-based amorphous phases. In this work, the effects of Ta content on the microstructure, mechanical properties, and soft magnetic performance of Fe-based amorphous alloys were systematically investigated. The results indicated that Ta remained uniformly dispersed within the FeSiB amorphous powder, and no new phases were formed after mechanical ball milling. The higher mixing enthalpy of Ta and its atomic radius difference from other elements (such as Fe, Si, B) were beneficial in improving glass-forming ability (GFA), and with an increase in Ta element content from 0% to 2%, 4% and 6%, the amorphous phase content was 48.6%, 51.5%, 60.4% and 54.8%, respectively. The average microhardness of the coating with a Ta content of 4% was 1310 HV0.2, which was 50HV0.2 higher than before; in addition, the wear rate reduced from 2.21 × 10−4 mg·N−1·m−1 to 2.06 × 10−4 mg·N−1·m−1. Also, corrosion tests showed that the coating with a Ta content of 4% displayed superior corrosion resistance compared to that before the Ta addition. However, because the element Ta could alter the local electronic environment and enhance the local magnetic anisotropy of FeSiB, the saturation magnetic flux density (Ms) decreased from 1.64 T to 1.56 T, and the coercivity (Hc) increased from 0.9 A/m to 1.3 A/m, which caused degradation of the soft magnetic properties.