Molecular beam epitaxy growth and optoelectronic properties of droplet-free lattice-matched GaInAsSbBi on GaSb with wavelength extension exceeding 5 μm

GaInAsSbBi alloys are grown lattice-matched on GaSb by molecular beam epitaxy demonstrating smooth surface morphologies, >5 μm wavelength photoluminescence emission, and minority carrier lifetimes >1 μs. At a growth temperature of 400 °C, the Ga flux is systematically increased and the Bi flux systematically decreased to identify GaInAsSbBi growth conditions that yield smooth droplet-free surface morphologies. The minority carrier lifetime is evaluated using time-resolved photoluminescence, where it is observed that GaInAsSbBi samples exhibit minority carrier lifetimes comparable to their Bi-free GaInAsSb counterparts, on the order of 1.5–2 μs. The bandgap and Urbach energy are evaluated from steady-state photoluminescence to gain insight into the impact of the incorporated Bi. Coupled with Rutherford backscattering spectrometry measurements of the Bi mole fraction, bandgap reduction rates of 97 meV/% Bi in InAsSbBi and 150 meV/% Bi in GaInAsSbBi are observed, significantly higher than previous evaluations in InAsSbBi (35–55 meV/% Bi). Detailed comparisons of the Bi mole fraction, bandgap energy, and Urbach energy indicate that the bandgap reduction potential in this alloy system is inhibited by the formation of Bi clusters; however, the inclusion of Ga in the quinary alloy is effective in suppressing Bi's tendency to incorporate in clusters for Ga mole fractions >9%, maximizing the bandgap reduction per unit Bi and overall optoelectronic quality.