The Influence of KCl and HCl on the High-Temperature Oxidation of a Fe-2.25Cr-1Mo Steel at 400 °C

The influence of alkali- and chlorine-containing compounds on the corrosion of superheater alloys has been studied extensively. The current paper instead investigates the corrosive effects of KCl and HCl under conditions relevant to waterwall conditions. A low-alloy (Fe-2.25Cr-1Mo) steel was exposed to KCl(s), 500 vppm HCl(g) and (KCl + HCl) in the presence of 5%O 2 and 20% H 2 O at 400 °C. The results indicate that alloy chlorination by KCl occurs by an electrochemical process, involving cathodic formation of chemisorbed KOH on the scale surface and anodic formation of solid FeCl 2 at the bottom of the scale. The process is accompanied by extensive cracking and delamination of the iron oxide scale, resulting in a complex, convoluted scale morphology. Adding 500 vppm HCl to the experimental environment (KCl + HCl) initially greatly accelerated the formation of FeCl 2 at the scale/alloy interface. The accelerated alloy chlorination is attributed to HCl reacting with KOH at the scale surface, causing the cathodic process to be depolarized. A rapid slowing down of the rate of chlorination and corrosion in KCl + HCl environment was observed which was attributed to the electronically insulating nature of the FeCl 2 layer which forms at the bottom of the scale, disconnecting the anodic and cathodic regions.