Corrosion inhibition of carbon steel in chloride solutions by blends of calcium gluconate and sodium benzoate

Inhibition efficiency of calcium gluconate, alone and in blends with sodium benzoate, on the corrosion of carbon steel in chloride solutions has been assessed by potentiodynamic polarization measurements and mass loss detection in the temperature range from 25 to 70 °C. Sodium benzoate efficient in hindering the general corrosion in chloride solutions can induce pitting of carbon steel. Along with decreasing the general corrosion calcium gluconate, an ecologically acceptable compound, eliminated the susceptibility to pitting formation. The inhibition of the anodic reaction by gluconate and benzoate, and the slowing down the cathodic reaction in solutions of calcium gluconate was confirmed. Korrosionsinhibierung von unlegiertem Stahl in Chloridlosungen durch Mischungen von Kalziumglukonat und Natriumbenzoat Die Inhibitorwirksamkeit des Kalziumglukonats allein oder in Mischungen mit Natriumbenzoat bezuglich der Korrosion von Kohlenstoffstahl in Chloridlosungen wurde erforscht, und zwar durch potentiodynamische Polarisationsmessungen und Massenverlustbestimmungen im Temperaturbereich von 25 bis 70 °C. Natriumbenzoat ist wirksam fur die Verhutung der allgemeinen Korrosion in Chloridlosungen aber kann Lochfrass von Kohlenstoffstahl auslosen. Nebst der Verzogerung der allgemeinen Korrosion beseitigt Kalziumglukonat, das auch okologisch annehmbar ist, die Neigung zur Lochfrassbildung. Die Inhibition der anodischen Reaktion durch Glukonate und Benzoate sowie die Verlangsamung der kathodischen Reaktion in Losungen des Kalziumglukonates wurden bestatigt.