Hierarchical Y and USY Zeolites Designed by Post‐Synthetic Strategies

This is the authors' abstract. We don't add key points for this paper.

Strategic combinations of affordable and scalable post‐synthetic modifications enabled to design a broad family of hierarchical Y and USY zeolites (FAU topology) independent on the Si/Al ratio. Pristine (Y, Si/Al = 2.4), steamed (USY, Si/Al = 2.6), and steamed and dealuminated (USY, Si/Al = 15 and 30) zeolites were exposed to a variety of acid (H 4 EDTA and Na 2 H 2 EDTA) and base (NaOH) treatments, which led to the introduction of mesopore surfaces up to 500 m 2 g −1 , while preserving the intrinsic zeolite properties. Pristine Y and USY zeolites (Si/Al ∼ 2.5) required mild dealumination (to Si/Al > 4 in the case of Y) to facilitate subsequent efficient desilication. Alkaline treatment of Y and USY zeolites with low Si/Al ratios (∼4–6) led to an abundance of Al‐rich debris, which could be removed by a subsequent mild acid wash. On the other hand, severely steamed and dealuminated, hence Si‐rich, USY zeolites (Si/Al = 15 and 30) proved extremely sensitive to the alkaline solution, displaying facile dissolution and substantial amorphization. For the latter group of ultra‐stable Y zeolites, the presence of TPA + in the alkaline solution enables to protect the zeolite structures upon the introduction of mesoporosity by desilication, preserving crystallinity and micropore volume. The sorption and catalytic properties of the hierarchical Y and USY zeolites were superior compared to the conventional counterparts.