Kinetics and thermodynamics of hydrolytic depolymerization of poly(ethylene terephthalate) at high pressure and temperature

Hydrolytic depolymerization of PET (polyethylene terephthalate) waste in excess of water was studied using a 0.5‐L stirred high‐pressure autoclave at temperatures of 100, 150, 200, and 250°C and at 200, 300, 400, 500, 700, and 800 psi (pounds per square inch) pressure. Velocity constants of hydrolysis were calculated from the experimental data obtained. Maximum depolymerization (91.38%) of PET into monomer was obtained at 250°C and 800 psi. pressure. However, the maximum rate of reaction was recorded at 200°C and 500 psi temperature and pressure, respectively. The energy of activation and frequency factor were calculated, as 64.13 KJ/g mol and 7.336 × 10 4 min −1 , respectively, for higher pressure and temperature conditions. It was also reported that the hydrolytic depolymerization is first order with the velocity constant 1.773 × 10 −2 min −1 at 250°C.