Nonlinear Absorption and Low-Threshold Multiphoton Pumped Stimulated Emission from All-Inorganic Perovskite Nanocrystals

Halide perovskite materials have attracted intense research interest due to the striking performance in photoharvesting photovoltaics as well as photoemitting applications. Very recently, the emerging CsPbX3 (X = Cl, Br, I) perovskite nanocrystals have been demonstrated to be efficient emitters with photoluminescence quantum yield as high as ∼90%, room temperature single photon sources, and favorable lasing materials. Herein, the nonlinear optical properties, in particular, the multiphoton absorption and resultant photoluminescence of the CsPbBr3 nanocrystals, were investigated. Notably, a large two-photon absorption cross-section of up to ∼1.2 × 10(5) GM is determined for 9 nm sized CsPbBr3 nanocrystals. Moreover, low-threshold frequency-upconverted stimulated emission by two-photon absorption was observed from the thin film of close-packed CsPbBr3 nanocrystals. The stimulated emission is found to be photostable and wavelength-tunable. We further realize the three-photon pumped stimulated emission in green spectra range from colloidal nanocrystals for the first time. Our results reveal the strong nonlinear absorption in the emerging CsPbX3 perovskite nanocrystals and suggest these nanocrystals as attractive multiphoton pumped optical gain media, which would offer new opportunities in nonlinear photonics and revive the nonlinear optical devices.