The demanding operational requirements of ultra-deep oil and gas exploration present formidable challenges for material performance, necessitating the development of novel cemented carbides that combine high strength-toughness with exceptional corrosion resistance. In this study, Cr2(C,N) was employed as a grain inhibitor to introduce N into the dual-scale structured WC-Co cemented carbide system for the fabrication of novel cemented carbides. The effects of Cr2(C,N) addition on the microstructural organization, mechanical properties and corrosion resistance behavior were systematically investigated. The experimental results show that the addition of Cr2(C,N) effectively prevents the direct contact of these coarse WC grains and allows more fine WC grains to be retained to fill the regions between these coarse WC grains and the Co binder phase, thereby suppressing Co pool formation and resulting in a continuous and uniform Co binder network. When the addition amount of Cr2(C,N) reaches 0.6 wt.%, the dual-scale structured cemented carbide achieves the optimal comprehensive mechanical properties, with a transverse rupture strength of 3182.3 MPa, a fracture toughness of 18.68 MPa·m1/2, and a hardness of 1140.4 HV30. Meanwhile, the optimization of microstructure, the formation of a passive film, and the stabilization of the fcc-Co phase jointly contribute to the superior corrosion resistance of this composition.
He et al. (Mon,) studied this question.