Anisotropic polyimide (PI)/graphene composite aerogels were fabricated by unidirectional freezing. A poly(amic acid) (PAA) ammonium salt/graphene dispersion was first synthesized by mixing together PAA, H₂O, triethylamine (TEA), and graphene and then was successively subjected to one-way freezing, freeze-drying, and thermal imidization. The one-way growth of ice crystals endowed the composite aerogels with highly arranged tubular pores. The PI/graphene composite aerogels possessed anisotropic conductivity, electromagnetic interference (EMI) shielding, heat transfer, and compression performance. Moreover, the composite aerogels with low density (0.076 g·cm⁻³) exhibited high EMI shielding effectiveness (SE) of 26.1-28.8 dB, and its specific EMI SE value achieved 1373-1518 dB·cm²·g⁻¹ when the graphene content was 13 wt %. The main electromagnetic interference shielding mechanism of these composite aerogels was microwave absorption. The composite aerogels had excellent thermal stability, and their 5% weight loss temperature was higher than 546 °C in nitrogen. This research provided an easy and environmentally friendly approach to prepare lightweight and anisotropic PI-based composite aerogels.
No takes yet. Share an insight, caveat, or question.
Yu et al. (2020) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: