Performance Evaluation of a Microhybrid Dental Restorative Composite Reinforced with Organoclay Nanoparticles

Dental restorative resins available today still have limitations that may affect their durability. This study explores reinforcing a universal microhybrid dental composite resin with organomodified nanoclay at low filler loadings (0, 0.5, 1, 3, and 5 wt%). The morphology, structural features, and light transmittance of the composites were analyzed using scanning electron microscopy (SEM), X-ray diffraction (XRD), attenuated total reflection–Fourier transform infrared (ATR–FTIR), and UV–Vis spectroscopy. The degree of conversion and polymerization shrinkage were measured with ATR–FTIR and a linear variable displacement transducer (LVDT). Water sorption and solubility parameters and flexural properties were assessed gravimetrically and with a dynamometer, respectively. The composites mainly showed exfoliated structures and an improved degree of conversion. Polymerization shrinkage and solubility were lower than those of unmodified dental resin. The highest degree of conversion was observed in composites with 0.5–1 wt% nanoclay. The incorporation of 1 wt% nanoclay resulted in the lowest shrinkage and sorption, along with the highest flexural modulus and strength. Overall, the results suggest that low nanoclay concentrations can improve the physicochemical and mechanical properties of dental composites, highlighting their potential to develop advanced restorative materials that can address current clinical challenges.