Perpendicular magnetic tunnel junction with tunneling magnetoresistance ratio of 64% using MgO (100) barrier layer prepared at room temperature

MgO (100) textured films can be prepared by reactive facing targets sputtering at room temperature without postdeposition annealing process when they were deposited on (100) oriented Fe buffer layers. This method allows fabrication of perpendicular magnetic tunnel junction (p-MTJ) with MgO (100) tunneling barrier layer and rare-earth transition metal (RE-TM) alloy thin films as perpendicularly magnetized free and pinned layers. The 3-nm-thick MgO tunneling barrier layer in p-MTJ multilayer prepared on glass substrate revealed (100) crystalline orientation. Extraordinary Hall effect measurement clarified that the perpendicular magnetic components of 3-nm-thick Fe buffer layers on the two ends of MgO tunneling barrier layer were increased by exchange coupling with RE-TM alloy layers. The RA of 35kΩμm2 and tunneling magnetoresistance ratio of 64% was observed in the multilayered p-MTJ element by current-in-plane-tunneling.