Hydrophobin gene deletion and environmental growth conditions impact mechanical properties of mycelium by affecting the density of the material

levels. This was accompanied by a maximum tensile strength (σ) of 5.1-9.6 MPa. In contrast, E and σ of the Δsc3 strain were 3-4- fold higher with values of 1237-2727 MPa and 15.6-40.4 MPa, respectively. These values correlated with mycelium density, while no differences in chemical composition of the mycelia were observed as shown by ATR-FTIR. Together, genetic modification and environmental growth conditions impact mechanical properties of the mycelium by affecting the density of the mycelium. As a result, mechanical properties of wild type mycelium were similar to those of natural materials, while those of Δsc3 were more similar to thermoplastics.