Influence of Annealing Cooling Method Prior to Final Cold Drawing on the Microstructure and Mechanical Properties of Al–Zn–Mg–Cu Alloy Wire

High-quality, large-weight alloy wires (>200 kg per coil) for aerospace fasteners require intermediate annealing prior to final cold drawing, as well as subsequent solution and aging heat treatments, which are critical processes during their manufacturing. However, the evolution of microstructure and mechanical properties during these procedures has not been systematically investigated. In this study, different cooling methods after intermediate annealing were comparatively investigated to clarify their influence on the microstructure evolution, precipitation behavior, and mechanical properties of Al–Zn–Mg–Cu alloy wires. The results revealed that the cold heading performance of alloy wires is determined by the strength–ductility balance, crystallographic texture, and precipitation behavior. Furnace cooling promoted η′ phase coarsening, resulting in lower strength and higher ductility, which enhanced deformation homogeneity and cold heading formability. The near-zero Δr reduced strain localization and cracking susceptibility, whereas higher Δr in water- and air-cooling samples increased anisotropy and cracking tendency. After heat treatment, strength differences became negligible, whereas elongation remained texture dependent, with the weaker texture in the furnace-cooling sample yielding superior ductility.