Laser Surface Hardening Characterisation of Metal Alloys with and Without Pre-Heat Treatment Impacting Industrial Innovations: A Critical Review

Laser surface hardening is a technique that improves various mechanical characteristics of different materials. The methods are being extensively used in the automobile, aerospace, tool manufacturing, and construction industries for various components. The present review highlights the hardness and hardened surface depth improvement of different steels and non-ferrous alloys in as-bought and pre-heat treatment conditions. Diode and fibre lasers have rendered higher surface hardness and hardened depth, while consuming higher power. Nd:YAG lasers have resulted in a precise increase in hardness and a very minimal 0.8 in ferrous and 2 mm in surface-hardened depth of non-ferrous alloys, proving a better efficiency. The pre-heat treatments are selected to enhance mechanical properties and reduce the deformations and defects. An increase of 300.43 and 282.38% of surface hardness due to laser hardening as compared to the core material of AISI 420 was observed using a high-power diode laser. A huge 281.41% of increase in surface hardness was observed for ICD-5 tool steel using Nd:YAG lasers. The annealing pre-heat treatment has also affected the hardenability, resulting in high hardness. Non-ferrous alloys such as titanium and A356 alloys have recorded 200 and 125% increase in surface hardness compared to their core using Nd:YAG lasers.