Study on the Tribocorrosion Behaviors of DLC-Si Films in aSeawater Environment

The performance requirements of wear-resistant and anti-corrosion coatings for marine equipment continue to increase. Diamond-like carbon (DLC) film has become a preferred protective material due to its high hardness, low friction and chemical inertia. To reveal the tribocorrosion mechanism of Si-doped DLC films in a seawater environment, a Cr-WC-WC/C transition layer and DLC-Si films with different Si contents were prepared by high-power pulsed magnetron sputtering (HiPIMS) technology on 304 stainless steel. The tribocorrosion tests were carried out under open-circuit potential and dynamic polarization conditions in seawater. The results show that Si doping improved the tribocorrosion resistance of the films. The sample with Si content of 9.26 at.% has the lowest self-corrosion current density, the smallest volume loss, complete wear scar morphology and no obvious substrate exposure. The strengthening mechanism is attributed to Si doping, which induces the formation of a SiOx passivation film and a hydrated silica gel lubrication layer. This establishes a synergistic solid-chemical lubrication system, inhibits sp2 cluster growth, prolongs the diffusion path of corrosive media, and mitigates the damaging wear–corrosion synergy. This study confirms that moderate Si doping can significantly improve the wear resistance and corrosion resistance of DLC films in a seawater environment, and provides a theoretical basis for the design and application of carbon-based protective coatings for marine equipment.