Microstructures and Mechanical Properties of Al-2Fe-xCo Ternary Alloys with High Thermal Conductivity

FeCo phases. The rolled Al-2Fe-0.3Co alloy exhibits the highest thermal conductivity, which is about 225 W/(m·K), approximately 11 % higher than the as-cast Al-2Fe sample. The ultimate tensile strength (UTS) and elongation (EL) of as-cast Al-2Fe-0.5Co (UTS: 138 MPa; EL: 22.0 %) are increased by 35 % and 69 %, respectively, compared with those of unmodified alloy (UTS: 102 MPa; EL: 13.0 %).