Comparison of Erosion Behavior and Particle Contamination in Mass-Production CF4/O2 Plasma Chambers Using Y2O3 and YF3 Protective Coatings

) etching. As examined by transmission electron microscopy, the Y₂O₃ and YF₃ coatings become oxyfluorinated after exposure to the plasma, wherein the yttrium oxyfluoride film formation was observed on the surface with a thickness of 5.2 and 6.8 nm, respectively. The difference in the oxyfluorination of Y₂O₃ and YF₃ coatings could be attributed to Y-F and Y-O bonding energies. X-ray photoelectron spectroscopy analyses revealed that a strongly fluorinated bonding (Y-F bond) was obtained on the etched surface of the YF₃ coating. Scanning electron microscopy and energy dispersive X-ray diffraction analysis revealed that the nanoparticles on the 12-inch wafer are composed of etchant gases and Y₂O₃. These results indicate that the YF₃ coating is a more erosion-resistant material, resulting in fewer contamination particles compared with the Y₂O₃ coating.