Influence of Graphene Oxide on Cement Hydration Products, Microstructure, and Mechanical Performance

This study examines the effects of graphene oxide (GO) on the hydration behaviour, microstructure, and mechanical properties of Portland cement-based materials. Cement pastes and mortars incorporating GO at dosages of 0.0005%, 0.005%, and 0.05% by weight of cement were analysed through thermogravimetric analysis (TGA), X-ray diffraction (XRD), scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM/EDS), and mechanical strength testing. TGA results indicate that GO exerts a time-dependent influence on cement hydration. At early ages, GO slightly retards hydration, evidenced by lower C–S–H and CH content in GO-containing samples at 2 and 7 days, attributed to water adsorption by its oxygen-containing functional groups. At later curing ages (28–90 days), TGA results show greater C–S–H and CH weight losses in GO-modified samples compared to the reference, consistent with GO acting as a water reservoir and nucleation site. XRD and SEM results confirm that GO incorporation leads to a reduction in CH crystal size, a denser and more homogeneous microstructure, and fewer pores and microcracks. Mechanical tests revealed that GO contents of 0.0005% and 0.05% produced the most significant improvements, with increases of up to 9% in compressive strength and 16% in flexural strength at 90 days compared with the control specimens. In summary, the incorporation of low GO dosages effectively refines cement microstructure, enhances long-term hydration, and improves mechanical performance, demonstrating GO’s potential as a strength- and durability-enhancing nanomaterial for cementitious composites.