Abstract This study aims to investigate the temperature-dependent structure of germanene prepared by atomic segregation epitaxy on an Ag(111) thin film surface. A germanene (7√7 × 7√7) superstructure, obtained upon heating at 500 °C followed by cooling at room temperature, transforms into a germanene (√109 × √109) superstructure after further annealing at 250 °C and subsequently evolves into the Ag–Ge surface alloy upon annealing at 350 °C, as evidenced from the thorough analysis by scanning tunneling microscopy, low-energy electron diffraction, and core-level (CL) photoemission spectroscopy. Angle-resolved CL spectra reveal that germanium preferentially occupies the topmost atomic layer, forming the (7√7 × 7√7) and (√109 × √109) superstructures. In contrast, germanium is distributed within at least a few layers for the striped incommensurate surface alloy phase. From angle-resolved photoemission spectroscopy, the electronic structures of the (7√7 × 7√7) and (√109 × √109) superstructures appear to be almost the same. Based on these considerations, the surface phase diagram of Ge/Ag(111)/Ge(111) has been constructed. These findings provide insights into the relationship between germanene thermal stability and Ge concentration at the surface region of Ag(111).
Yuhara et al. (Wed,) studied this question.